SOWA Co., Ltd.

 

Examples

deburring

before

after

grinding condition
materialADC12
S6000 min-1
F1000 mm/min
D0.5mm

 

before

after

grinding condition
materialaluminum alloy
S6000 min-1
F1000 mm/min
D0.5mm

 

removing tool mark

before

Ra 0.546µm, Rz 2.169µm

after

Ra 0.097µm, Rz 0.441µm

grinding condition
materialSCM440
S6000 min-1
F1000 mm/min
D0.5mm

 

before

Ra 0.183µm, Rz 0.932µm

after

Ra 0.047µm, Rz 0.211µm

grinding condition
materialSUS303
S3000 min-1
F800 mm/min
D0.5mm

 

before

Ra 0.785µm, Rz 3.156µm

after

Ra 0.265µm, Rz 0.982µm

grinding condition
materialtitanium
S6000 min-1
F1000 mm/min
D0.5mm